Evaluation of mechanical properties of anatomically customized fiber posts using E-glass short fiber-reinforced composite to restore weakened endodontically treated premolars.

OBJECTIVE: This study was conducted to assess the influence of combining different forms of fiber-reinforced composites (FRC) on the mechanical behavior and bond strength of compromised endodontically treated teeth (ETT). MATERIALS AND METHODS: Eighty extracted human premolar teeth were randomly divided into five experimental groups according to the type of intra-radicular restoration and the canal preparation design which was either non-flared (Group 1), flared (Groups 2-5), closed-apex (Groups 1,3,5) or open-apex (Groups 2,4). Standard prefabricated fiber posts were used as intra-radicular restoration for Groups 1-3 while Groups 4-5 were restored with anatomically customized relined fiber posts. After composite core fabrication, all samples were sent for an artificial aging process. Fracture resistance and push-out bond strength tests were then carried out through a universal testing machine followed by mode of failure analysis via a stereomicroscope and scanning electron microscope. RESULTS: Pairwise Log-Rank comparisons revealed that the survival rate of Group 2 and Group 3 was significantly lower than all other groups after artificial aging. The highest fracture resistance value (1796 N) was recorded in Group 5 and was significantly higher than that of the other groups (p < 0.05), while Group 2 exhibited the lowest fracture resistance (758 N), which was significantly lower compared to the other groups. Group 5 and Group 4 demonstrated a significantly higher push-out bond strength, at all root thirds, than Group 3, Group 2, and Group 1 (p < 0.05). The most frequently observed failure mode in the tested groups occurred between the resin cement and radicular dentin. CONCLUSION: The use of short fiber-reinforced composite (SFRC) to reline the prefabricated FRC post has been proven to have superior fracture resistance with favorable failure patterns and increased push-out bond strength values compared to standard prefabricated FRC posts.

Combined Effects of Glutaraldehyde-based Desensitizer and Nd: YAG Laser on Dentinal Tubules Occlusion.

AIM: The aim of this study was to assess the impact of Nd:YAG laser, glutaraldehyde-based desensitizer (GD), or their combination on occluding dentinal tubules. MATERIALS AND METHODS: Fifty dentin samples were obtained from non-carious human third molars and randomly divided into five groups (n = 10): (1) Control group treated with 37% phosphoric acid, (2) GD group, (3) Nd:YAG laser group (1064 nm, 100 µs, 10 Hz, 300 µm fiber, 1 W power, 100 mJ energy, and 85 J/cm2 energy density), (4) GD followed by Nd:YAG laser group, and (5) Nd:YAG laser followed by GD group. Scanning electron microscopy (SEM) was used to capture five images from each sample for analysis of dentinal tubules using Image J software. SEM/EDX elemental analysis was performed to determine the main mineral contents. Data analyzed using one-way ANOVA and Tukey's post hoc test for statistical comparisons. RESULTS: Laser and combination groups showed a significant decrease in dentinal tubule counts compared with the control and GD groups (p < 0.0001). There were no significant differences in open dentinal tubule counts between the control and GD groups, as well as between the laser and combination groups. However, significant differences were observed in the total area, average size of the tubules, and percentage area between the control group and the treatment groups (GD, laser, GD + laser, laser + GD). No significant difference was found in the Ca/P ratio between the tested groups. CONCLUSION: The use of Nd:YAG laser alone or in combination with GD was more effective in occluding dentinal tubules compared to GD alone. CLINICAL SIGNIFICANCE: This study has shown that Nd:YAG laser alone and in combination with GD has superior dentinal tubule occlusion in vitro. Its clinical use in the treatment of dentinal hypersensitivity may overcome the drawback of conventional treatment approaches for dentin hypersensitivity needing repeated applications to achieve continuous relief from pain since acidic diet and toothbrushing result in the continuing elimination of precipitates and surface coatings. How to cite this article: Alzarooni AH, El-Damanhoury HM, Aravind SS, et al. Combined Effects of Glutaraldehyde-based Desensitizer and Nd: YAG Laser on Dentinal Tubules Occlusion. J Contemp Dent Pract 2024;25(1):52-57.

Contemporary Role and Applications of Artificial Intelligence in Dentistry.

Artificial Intelligence (AI) technologies play a significant role and significantly impact various sectors, including healthcare, engineering, sciences, and smart cities. AI has the potential to improve the quality of patient care and treatment outcomes while minimizing the risk of human error. Artificial Intelligence (AI) is transforming the dental industry, just like it is revolutionizing other sectors. It is used in dentistry to diagnose dental diseases and provide treatment recommendations. Dental professionals are increasingly relying on AI technology to assist in diagnosis, clinical decision-making, treatment planning, and prognosis prediction across ten dental specialties. One of the most significant advantages of AI in dentistry is its ability to analyze vast amounts of data quickly and accurately, providing dental professionals with valuable insights to enhance their decision-making processes. The purpose of this paper is to identify the advancement of artificial intelligence algorithms that have been frequently used in dentistry and assess how well they perform in terms of diagnosis, clinical decision-making, treatment, and prognosis prediction in ten dental specialties; dental public health, endodontics, oral and maxillofacial surgery, oral medicine and pathology, oral & maxillofacial radiology, orthodontics and dentofacial orthopedics, pediatric dentistry, periodontics, prosthodontics, and digital dentistry in general. We will also show the pros and cons of using AI in all dental specialties in different ways. Finally, we will present the limitations of using AI in dentistry, which made it incapable of replacing dental personnel, and dentists, who should consider AI a complimentary benefit and not a threat.

Wear, Fatigue and Fracture Resistance of Different Monolithic CAD/CAM Onlays As Abutments for Acetal Resin or Cobalt-Chromium Removable Partial Denture Frameworks.

PURPOSE: To assess wear, fatigue, and fracture resistance of different CAD/CAM onlays, milled from monolithic Zirconia (Zr), hybrid ceramic (EN), and lithium disilicate (LS), when used as abutments for removable partial denture frameworks fabricated from acetal resin (AR) or cobalt-chromium (Co-Cr). METHODS: Standard onlays and RPD framework were designed and milled using CAD/CAM. Onlays were cemented with resin cement to identical teeth models. The RPD's occlusal rest surface and the ceramic onlays' rest seats were both 3D scanned before and after 750,000 mechanical load cycles (50 N) and 8,000 thermal cycles (5-55°C) in a chewing simulator. The volumetric loss was measured using 3D image processing software, and the failure of the samples was detected using a stereomicroscope. The fracture resistance was tested by loading to failure in a universal testing machine. The fatigue failure results were analyzed with Fisher's exact probability test and the wear and fracture resistance data were analyzed using two-way ANOVA and Bonferroni Post-hoc test (P<0.05). RESULTS: A significant difference (p<0.05) was found between the tested experimental groups in wear, fatigue, and fracture resistance. Zr/Co-Cr combinations exhibited the least wear and the highest fatigue and fracture resistance (P<0.05), while the highest wear and least fatigue and fracture resistance were recorded for EN/AR group (p<0.05). CONCLUSIONS: Zr onlays demonstrated a conservative treatment option with superior mechanical behavior when used as an onlay abutment, regardless of the RPD framework material used. The AR framework is not recommended in the posterior region for removable partial dentures.

Effect of Thickness and Bonding Technique on Fatigue and Fracture Resistance of Feldspathic Ultra-Thin Laminate Veneers.

OBJECTIVES: To evaluate the fatigue and fracture resistance of ultra-thin laminate veneers (UTLV) with two different thicknesses and two different bonding protocols. MATERIALS AND METHODS: A total of 64 flat enamel surfaces were assigned to either 0.2 or 0.4 mm UTLV. The UTLV were further subdivided and assigned to one of two bonding techniques: adhesive resin cement(RC( or preheated restorative resin composite (HC) (n = 16). Eight samples were fatigued with 750,000 mechanical cycles and 8,000 thermal cycles between 5 and 55°C in a chewing simulator, and the failure mode was evaluated using a stereomicroscope and SEM. The other eight samples from each group were loaded to failure in a universal testing machine to test the fracture resistance. Fisher's exact Probability test was used to analyze the fatigue test results, and two-way analysis of variance and Bonferroni's test were used to analyze the fracture resistance test results. RESULTS: The difference in fatigue resistance between failure proportions in different groups was statistically different (p < 0.05). The 0.4-mm-thick UTLV had similar results regardless of the bonding technique, while 0.2-mm-thick UTLV only showed comparable results when cemented with preheated HC. No statistically significant difference was found in fracture resistance between the tested groups (p > 0.05). CONCLUSION: The Bonding technique and the thickness of the UTLV had impacted fatigue resistance but had no significant effect on the fracture resistance. bonding of UTLV with preheated composite increases their fatigue resistance. Different testing approaches delivered different results.

2D and 3D Wear Analysis of 3D Printed and Prefabricated Artificial Teeth.

PURPOSE: This study aimed to assess the 3-body wear of prefabricated and 3D-printed artificial denture teeth. MATERIALS AND METHODS: Four groups of artificial teeth were used; 3D-printed polymethylmethacrylate (PMMA) teeth (PR) and 3 prefabricated commercially available denture teeth: PMMA (Gnathostar, GN), PMMA (SR Orthotyp PE, SR), and Nanohybrid composite (SR Phonares NHC, PH). The 3-body wear test was performed using a steatite ceramic antagonist in a chewing simulator with 750,000 cycles, temperature 23 ± 2 ˚C, and force of 50 N. The abrasive medium was composed of ground millet seeds and white rice mixed with distilled water. The teeth were 3D-scanned before and after the wear test. The 3D images were assessed for teeth wear by measuring the volumetric (3D wear) and the vertical (2D wear) substance loss. The one-way analysis of variance followed by Tukey post hoc test was used to statistically obtain the data analysis. RESULTS: Maximum 3D wear was observed in the PR (51.05 ± 4.53 mm³), followed by GN (20.22 ± 6.29 mm³) and SR (12.12 ± 6.29 mm³) artificial teeth. Minimum wear occurred in the PH teeth (6.24 ± 0.87 mm³). The analytical differences amongst the groups were statistically significant (P < .05) except between PH and SR teeth. For 2D wear measurement, the maximum was seen in the GN teeth (6.29 ± 1.64 mm), followed by PR (5.04 ± 0.83 mm) and then SR (4.53 ± 0.87 mm). The PH teeth (3.09 ± 0.68 mm) again showed minimum wear. Statistically, amongst the groups, the major observable differences (P < .05) were between PH and GN, PH and PR, and SR and GN. CONCLUSIONS: Composite resin teeth had a greater wear resistance than acrylic resin teeth and 3D-printed resin teeth, both of which were comparable. Due to the advancement of digital workflows, manufacturers should devote effort to enhancing 3D-printed teeth.

Surface Properties and Wear Resistance of Injectable and Computer-Aided Design/Computer Aided Manufacturing-Milled Resin Composite Thin Occlusal Veneers.

OBJECTIVES: This study was conducted to investigate the microhardness, surface roughness (Ra), and wear behavior of thin occlusal veneers (TOV) fabricated from different injectable composite materials and compare them to a Computer-Aided Design (CAD)/Computer-Aided Manufacturing (CAM) resin-based material. MATERIALS AND METHODS: A 1-mm occusal veneer preparation was done in a mandibular right second molar typodont tooth. The prepared model was duplicated to fabricate 32 replicas and divided into four groups (n = 8). Standard TOV were fabricated either indirectly from Cerasmart blocks, Cerasmart, GC (CS), or directly from Beautifil Injectable X, Shofu (BF), G-ænial Universal injectable, GC (GU), or SonicFill 2, Kerr (SF) using the injection molding technique. All the specimens were subjected to both thermomechanical cyclic loading (TMC) in a chewing simulator. Wear measurement was conducted by three-dimensional (3D) scanning of the veneered models before and after TMC, and the difference in the volume of the sample was recorded as the volumetric material loss due to wear. Ra before and after TMC and Vickers microhardness (VHN) of the tested materials were measured using standardized samples (n = 8). Representative samples from each group were investigated under a stereomicroscope and a scanning electron microscope. STATISTICAL ANALYSIS: One-way analysis of variance (ANOVA) was applied to detect the effect of material on VHN and wear. Two-way ANOVA was utilized to examine the impact of material and TMC on Ra. Multiple comparisons between the groups were conducted using Tukey's post hoc test (α = 0.05). The Pearson's correlation coefficient was used to determine the relationship between hardness and wear and between roughness and wear (α = 0.05). RESULTS: CS exhibited the highest mean VHN (p ≤ 0.001), followed by GU and SF which were statistically similar (p = 0.883) but significantly higher than BF (p < 0.001). After TMC, GU revealed the lowest Ra and volumetric wear (VW), followed by CS, BF, and SF (p < 0.5). A highly significant correlation existed between Ra and VW (p = 0.001, R 2 = 0.9803). CONCLUSION: The effect of TMC on the surface properties and wear resistance of the investigated TOV is material-dependent. GU injectable TOV are less influenced by TMC than CS milled TOV. In contrast, BF and SF demonstrated significant VW and Ra which might limit their clinical use as TOV.

Er:YAG Laser Debonding of Lithium Disilicate Laminate Veneers: Effect of Laser Power Settings and Veneer Thickness on The Debonding Time and Pulpal Temperature.

Introduction: Er:YAG laser is a non-destructive tool for debonding of laminate veneers. This study investigated the effect of different laser powers on the pulp temperature and the time required to perform the debonding of lithium disilicate laminate veneers with different thicknesses. Methods: The labial enamel of 48 maxillary central incisors was flattened and polished. The teeth were restored with flat lithium disilicate ceramic veneers (4.0 mm×6.0 mm) with one of two different thicknesses (0.5 and 1.0 mm). Veneer debonding was performed with an Er:YAG laser with a wavelength of 2940 nm, pulse duration of 100 µm (VSP mode), 10 Hz, and one of the three laser power settings: 1.5 W (150 mJ), 3.0 W (300 mJ). and 5.4 W (540 mJ) (n=8). Veneer detachment time and intra-pulp temperature change (ΔT) were measured. Statistical analysis was performed using the two-way ANOVA and Bonferroni's post hoc test (α=0.05). The correlation between debonding time and temperature change was calculated using Pearson's correlation. Results: The longest time was recorded to remove the 1.0-mm veneer at 1.5 W (P<0.05) and the shortest time was recorded when deboning the 0.5 mm veneer with 5.4 W (P<0.05). ΔT decreased significantly with increasing laser power. A low correlation was found between time and ΔT (R2=0.113). Conclusion: Laser power and veneer thickness are important factors for veneer debonding; thinner veneers are removed faster. When debonding thick veneers, 5.4W laser power is more efficient and causes fewer changes to the pulp temperature.

Fracture resistance and failure mode of layered translucent zirconia with different crown designs.

This study investigated the impact of different veneering design on the fracture resistance and failure mode of layered translucent zirconia crowns, compared to the full monolithic zirconia crowns. Ninety crowns with different designs were divided into six groups (n=15); one fully contoured monolithic crown (FMC), one fully veneered with porcelain (FVC), or four partially veneered designs. All crowns were thermo-cycled, and then loaded to failure in a universal testing machine. The fracture resistance (N) and fracture modes were assessed. One-way ANOVA was performed followed by Tukey's multiple comparison (α<0.05). Results demonstrated that all the tested partially veneered designs exhibited enhanced fracture resistances and were comparable to that of the full-contour monolithic translucent zirconia crowns.

Influence of Low-Level Laser Modification and Adhesive Application Mode on the Bonding Efficiency of Universal Adhesives to Er:YAG Laser-Ablated Dentin.

Introduction: Erbium laser ablation as a method of tooth preparation and conditioning has shown promising results. Although previous studies have adopted various combinations of different laser parameters and several dentin adhesive systems, very few have investigated combining high-level and low-level ER:YAG lasers with Universal adhesives. This study aimed to assess the impact of using low-energy irradiation on the surface micro-topography and shear bond strength (SBS) of universal adhesive (UA) to the erbium:yttrium-aluminum-garnet (Er:YAG) laser-ablated dentin substrate, bonded in etch-and-rinse or self-etch adhesive mode. Methods: Eighty-seven extracted molars were sectioned to expose flat occlusal dentin surface; 60 teeth were divided equally into three groups according to the surface treatment; bur-cutting (B), Er:YAG high-energy laser cutting (L1 - 200 mJ, 20 Hz, 50 µs pulse), or L1 followed by low-energy laser modification (L1 /L2 - 80 mJ, 10 Hz, 50 µs pulse). Then each group was equally divided into two groups (n=10) according to the mode of application of the universal adhesive; either etch-and-rinse (ER) or self-etching (SE). The samples were subjected to thermocycling (5000 cycle between 5°C and 55°C), and SBS was tested. Two-way ANOVA and Tukey post hoc test were used to analyze the results. The remaining 27 samples were used to investigate the effect of the treatment on the topography of the treated dentin surfaces using a scanning electron microscope (SEM). Results: B/SE recorded the highest SBS (25.48 ± 2.6 MPa) followed by B/ER (23.20 ± 6.8 MPa) and L1 /L2 /SE (22.94 ± 4.1 MPa) and with no statistically significant difference between these groups (P >0.05). The lowest SBS results (P <0.05) were recorded for L1/SE (12.22 ± 3 MPa). No statistical differences were found between the SBS of L1 /L2 /ER and L1 /ER groups or between the SBS of L1 /L2 / ER and L1 /L2 /SE groups. Conclusion: A subsequent treatment of the Er:YAG laser-ablated dentin with low-energy laser modification mode (LMM) enhances the SBS of the tested UA when applied in SE mode.

In Vitro Enamel Remineralization Efficacy of Calcium Silicate-Sodium Phosphate-Fluoride Salts versus NovaMin Bioactive Glass, Following Tooth Whitening.

OBJECTIVES: This study aimed to evaluate the effect of in-office bleaching on the enamel surface and the efficacy of calcium silicate-sodium phosphate-fluoride salt (CS) and NovaMin bioactive glass (NM) dentifrice in remineralizing bleached enamel. MATERIALS AND METHODS: Forty extracted premolars were sectioned mesio-distally, and the facial and lingual enamel were flattened and polished. The samples were equally divided into nonbleached and bleached with 38% hydrogen peroxide (HP). Each group was further divided according to the remineralization protocol (n = 10); no remineralization treatment (nontreated), CS, or NM, applied for 3 minutes two times/day for 7 days, or CS combined with NR-5 boosting serum (CS+NR-5) applied for 3 minutes once/day for 3 days. The average Knoop hardness number (KHN) and surface roughness (utilizing atomic force microscopy) were measured. Surface topography/elemental analysis was analyzed by using scanning electron microscopy/energy dispersive X-ray analysis. All the tests were performed at baseline, after bleaching, and following each remineralization protocol. Data were statistically analyzed by two-way analysis of variance and Bonferroni post hoc multiple comparison tests (α = 0.05). RESULTS: HP significantly reduced KHN and increased roughness (p < 0.05). All remineralization materials increased the hardness and reduced the surface roughness after bleaching except NM, which demonstrated significantly increased roughness (p < 0.05). Ca/P ratio decreased after bleaching (p < 0.05), and following treatment, CS and CS+NR-5 exhibited higher remineralization capacity in comparison to NM (p < 0.05). CONCLUSION: Although none of the material tested was able to reverse the negative effect of high-concentration in-office HP on enamel completely, the remineralization efficacy of CS and CS+NR-5 was superior to that of NM.

Adhesive luting to hybrid ceramic and resin composite CAD/CAM Blocks:Er:YAG Laser versus chemical etching and micro-abrasion pretreatment.

PURPOSE: To evaluate the effect of Er:YAG laser on the roughness, surface topography, and bond strength to resin luting cement based on chemical and micro-abrasion pretreatments of different computer-aided design/computer-aided manufacturing materials. METHODS: A polymer-infiltrated-ceramic-network (PICN) material (Vita Enamic, VE), three indirect resin composite (Cerasmart, CS; Shofu HC, SH; Lava Ultimate, LU), and one lithium disilicate ceramic (IPS e.max CAD, EM) blocks were subjected to one of the following pretreatments: no treatment (NC ), Er:YAG etching with one of two powers (either 3 or 6 W), hydrofluoric acid (HF) etching, self-etching ceramic primer (ME), or micro-abrasion (MA). The shear bond strength (SBS) of resin luting cement to pretreated materials was tested. Surface roughness was measured via atomic force microscopy, and surface topography was analyzed via scanning electron microscopy. Two-way analysis of variance, Tukey post-hoc test, and Pearson correlation were applied. RESULTS: Etching EM and VE with HF or the ME resulted in the highest SBS values in their groups (P < 0.05). LU, SH, VE, and CS indicated similar SBS values when treated with 3 W, 6 W, and MA. The highest surface roughness (Sa ) values were obtained for the LU, CS, and VE groups when treated with 6 W, whereas the lowest Sa values were obtained for CS when treated with the ME and EM when treated with the ME or 3 W. Only SH and CS indicated a significant correlation between surface rough ness and bond strength. CONCLUSIONS: Er:YAG laser etching is comparable to micro-abrasion when treating resin composite blocks and may induce fewer surface cracks. HF etching remains the gold standard for the treatment of glass-based ceramics and PICNs.

Behavioral management using sequenced treatment paradigm and audiovisual distraction during dental treatment in children with attention deficit/hyperactivity disorder.

OBJECTIVE: The present study aimed to assess behavioral management using sequenced treatment approach and audiovisual distraction (AVD) with/without video eyewear during dental procedure in children with attention deficit/hyperactivity disorder (ADHD). MATERIALS AND METHODS: This clinical trial included 31 children (n = 21 boys; n = 10 girls), aged between 6.5 and 8.1 years, distributed into Group A (n = 17, children not on ADHD medication) and Group B (n = 14, children taking medication for ADHD symptoms). The study involved four sessions, 1 week apart. Sessions I and II included behavioral management assessment and dental screening, respectively, while participants watched cartoon movie using an AV distracter with/without a video eyewear. During Sessions III and IV, dental prophylaxis and sealants were placed on first permanent molars, respectively, for both upper and lower jaws in both the groups. During the procedure, children were distracted with AV distracter with/without a video eyewear, and the mean changes in blood oxygen saturation (SaO2) and pulse rate were recorded every 5 min. Independent samples t-test was used, assessing for significant changes in pulse rate and SaO2 during each visit in both groups. RESULTS: Almost 95% (n = 113) of the first permanent molars showed signs of pit and fissure demineralization of varying severities, classified as the International Caries Detection and Assessment System-codes 1-3. During Session IV, there were significant differences (P ≤ 0.03 and P ≤ 0.05) in mean pulse rate in both groups of children, respectively, during fissure sealants or preventive resin restoration application on their permanent molars while being distracted using AVD with video eyewear. CONCLUSION: Our study recommends splitting of dental visits into multiple short sessions and video eyewear distraction for optimum behavioral management during dental procedures of children with ADHD.

Self-etching ceramic primer versus hydrofluoric acid etching: Etching efficacy and bonding performance.

AIM: This study assessed the effect of pretreatment of hybrid and glass ceramics using a self-etching primer on the shear bond strength (SBS) and surface topography, in comparison to pretreatment with hydrofluoric acid and silane. METHODS: 40 rectangular discs from each ceramic material (IPS e.max CAD;EM, Vita Mark II;VM, Vita Enamic;VE), were equally divided (n=10) and assigned to one of four surface pretreatment methods; etching with 4.8% hydrofluoric acid followed by Monobond plus (HFMP), Monobond etch & prime (Ivoclar Vivadent) (MEP), No treatment (NT) as negative control and Monobond plus (Ivoclar Vivadent) with no etching (MP) as positive control. SBS of resin cement (Multilink-N, Ivoclar Vivadent) to ceramic surfaces was tested following a standard protocol. Surface roughness was evaluated using an Atomic force microscope (AFM). Surface topography and elemental analysis were analyzed using SEM/EDX. Data were analyzed with two-way analysis of variance (ANOVA) and post-hoc Bonferroni test at a significance level of α=0.05. RESULTS: Pretreatment with HFMP resulted in higher SBS and increased surface roughness in comparison to MEP and MP. Regardless the method of surface pretreatment, the mean SBS values of EM ceramic was significantly higher (p<0.05) than those recorded for VM and VE, except when VE was treated with MEP, where the difference was statistically insignificant. Traces of fluoride ion were detected when MEP was used with VE and VM. CONCLUSION: Under limited conditions, using MEP resulted in comparable SBS results to HFMP; meanwhile HFMP remains the gold standard for pretreatment of glass ceramics for resin-luting cementation.

The effect of immediate dentin sealing and optical powder removal method on the fracture resistance of CAD/CAM-fabricated endocrowns.

OBJECTIVES: To evaluate the effect of immediate dentin sealing and optical powder removal method on the fracture resistance of CAD/CAM-fabricated ceramic endocrowns. MATERIALS AND METHODS: Seventy-eight extracted premolars were endodontically treated. Standardized endocrown preparations were done in 60 teeth. Teeth were divided equally (n = 10) depending on the treatment of dentin (delayed sealing [DS] or immediate sealing [IS]), and the methods of optical powder removal (air-water spray washing [AW]; microabrasion [MA]; or aqueous suspension of pumice [PB], followed by air-water spray washing). After cementation, specimens were thermocycled (5,000 cycles, 5°C/50°C) and stored in distilled water for 1 week. Specimens were loaded in compression using a universal testing machine until failure. Failure load was recorded, and modes of failure were examined under a stereomicroscope. Micromorphological evaluation of different dentin treatments was done under SEM (n = 3). Results were analyzed using two-way ANOVA and Bonferroni post hoc multiple comparison tests (α = 0.05). RESULTS: Fracture resistance of all IS groups was significantly lower than DS groups, except for AW. There was no statistically significant difference between powder removal methods. CONCLUSION: Immediate dentin sealing does not improve the fracture resistance of endocrown restorations. Air-water spray washing is adequate to remove the optical powder after optical scanning impression taking.

Effectiveness of teaching International Caries Detection and Assessment System II and its e-learning program to freshman dental students on occlusal caries detection.

OBJECTIVE: To assess the feasibility of teaching International Caries Detection and Assessment System (ICDAS) II and its e-learning program as tools for occlusal caries detection to freshmen dental students in comparison to dental graduates with 2 years of experience. MATERIALS AND METHODS: Eighty-four freshmen and 32 dental graduates examined occlusal surfaces of molars/premolars (n = 72) after a lecture and a hands-on workshop. The same procedure was repeated after 1 month following the training with ICDAS II e-learning program. Validation of ICDAS II codes was done histologically. Intra- and inter-examiner reproducibility of ICDAS II severity scores were assessed before and after e-learning using (Fleiss's kappa). RESULTS: The kappa values showed inter-examiner reproducibility ranged from 0.53 (ICDAS II code cut off ≥ 1) to 0.70 (ICDAS II code cut off ≥ 3) by undergraduates and 0.69 (ICDAS II code cut off ≥ 1) to 0.95 (ICDAS II code cut off ≥ 3) by graduates. The inter-examiner reproducibility ranged from 0.64 (ICDAS II code cut off ≥ 1) to 0.89 (ICDAS II code cut off ≥ 3). No statistically significant difference was found between both groups in intra-examiner agreements for assessing ICDAS II codes. A high statistically significant difference (P ≤ 0.01) in correct identification of codes 1, 2, and 4 from before to after e-learning were observed in both groups. The bias indices for the undergraduate group were higher than those of the graduate group. CONCLUSIONS: Early exposure of students to ICDAS II is a valuable method of teaching caries detection and its e-learning program significantly improves their caries diagnostic skills.